SUNPASS Fiberglass cloth is woven from twisted yarn and undergoes heat treatment to ensure superior performance. During this process, organic residues are completely burned out, resulting in high flexibility and minimal shrinkage. This makes the material ideal for applications where smoke emission is strictly prohibited.
Fiberglass cloth Applications：
Composite Reinforcement – Used in aerospace, automotive, and marine industries to strengthen lightweight composite structures.
PCB Manufacturing – Serves as a base material for printed circuit boards (PCBs), providing insulation and mechanical stability.
Thermal Insulation – Applied in high-temperature environments (e.g., furnaces, exhaust systems) for heat resistance.
Fireproofing – Incorporated into protective gear, curtains, and building materials for flame retardancy.
Surface Protection – Acts as a durable overlay for coatings or laminates in industrial and construction settings.
Fiberglass cloth Applicable Working Medium:
Used at 1000degree F/ 537degree C continuous
Heat treatment to burn out organic i.e. starch or silane on fabrics
Used in places where no smokes allowed
A high-performance very high temperature fabric, used in almost all industries for heat protection.
Fiberglass cloth Specifications:
|
Property |
Description |
Valvue |
|
|
English |
Metric |
||
|
Weave Style |
Satin |
- |
- |
|
Thickness |
- |
0.03inch |
0.8mm |
|
Weight |
- |
26oz/yd2 |
880g/m2 |
|
Widths |
- |
40-60inch |
1-1.5m |
|
Warp, Ends |
- |
46inch |
1m |
|
Fill, Ends |
- |
35inch |
0.9m |
|
Tensile Strength, Initial |
Warp |
630ibs/in |
112.6kg/cm |
|
Fill |
490ibs/in |
87.4kg/cm |
|
|
After 3 Hours at 1300ºF (700ºC) |
Warp |
360ibs/in |
64.2kg/cm |
|
Fill |
240ibs/in |
42.9kg/cm |
|
|
Temperature Resistance |
Maximum Continuously |
1022℉ |
550 °C |
|
Thermal Conductivity |
- |
0.09w/m-k |
|
|
Elongation |
- |
80% |
|
For more products, please visit it tenglongsealingss.com